Anticorrosive Epoxy Primer 1:1

2K DTM Epoxy Primer & Sealer

Variants

ColourArt. No.CapacityQuantity per carton
grey182461 l6
white182441 l6
black182451 l6
hardener182481 l6
grey182423,6 l4
white182403,6 l4
black182413,6 l4
hardener182433,6 l4

Gloss grade

matt
Anticorrosive Epoxy Primer 1:1

Technical documentation

Description

2K high performance epoxy primer with anticorrosive additives for car body repair. It can be applied directly to bare metal, effectively protecting steel surfaces from corrosion. It delivers very strong adhesion to various substrates and great sealing properties. Especially suited for use as a non-sanding wet-on-wet sealer, enabling fast and efficient repairs. Guarantees excellent protection of steel surfaces, very strong adhesion and easy application. Available in white, grey and black.

Important informations

  • Przetrzeć odtłuścić

    degrease

  • Proporcje mieszania

    Mixing ratio
    1 : 1

  • Lepkość natryskowa

    Spraying viscosity
    18 ÷ 20 s / 20°C

  • Żywotność mieszanki

    Pot life
    ~ 3 h / 20°C

  • Liczba warstw

    1 ÷ 3 layers
    HVLP / RP
    ø1,2 ÷ 1,5 mm

  • Czas odparowania

    between layers
    5 ÷ 10 min

  • Czas odparowania

    before baking
    ~ 10 min

  • Czas utwardzania

    Hardening time
    5 h / 20°C
    35 min / 60°C

Application process

  • Zastosowanie
  • Use

    For car repairs, as an isolating primer, for sanding or wet on wet application.

  • Proporcje mieszania
  • Mixing ratio by volume

    Primer: 1
    Hardener: 1
    Thinner: not required!

    Stir thoroughly until obtaining a homogenous mixture.

  • Lepkość natryskowa
  • Spraying viscosity

    18 ÷ 20 seconds at 20°C.

  • Żywotność mieszanki
  • Pot life for the mixture

    about 3 hours at 20°C

  • Liczba warstw
  • Number of layers
    • For wet on wet: 1,5 ÷ 2 layers; about 25 ÷ 50 µm of dry layer.
    • For sanding: 2 ÷ 3 layers; 100 ÷ 140 µm of dry layer.

    Gun parameters:
    RP nozzle: 1,2 ÷ 1,6 mm; Pressure of input: 2,0 ÷ 2,2 bars.
    HVLP nozzle: 1,3 ÷ 1,5 mm; Inlet pressure: 2,0 bars.

  • Czas odparowania
  • Evaporation time

    Between layers: 5 ÷ 10 minutes
    Before baking: about 10 minutes
    Before topcoating (wet on wet): 45 ÷ 60 minutes

    Evaporation time depends on the temperature and the number of layers.

  • Czas utwardzania
  • Hardening time
    • about 5 hours at 20°C (depending on coating thickness).
    • about 35 minutes at 60°C (depending on coating thickness).

    Temperature below 20°C significantly increases the hardening time.

  • Suszenie promieniem IR
  • IR drying

    8 ÷ 10 minutes under short wave for a coating thickess of 100 ÷ 140 µm. Do not exceed maximum temperature of 60°C. Use according to the recommendations of the equipment manufacturer. Wait about 10 minutes before starting IR drying.

  • Szlifowanie na sucho
  • Dry sanding

    Sanding paper P400 ÷ P500
    Wet on wet application does not require sanding!

  • Szlifowanie na mokro
  • Wet sanding

    Machine sanding: P600 ÷ P1000.
    Manual sanding: P800 ÷ P1000.

    Wet on wet application does not require sanding!

  • Informacja
  • Further work

    2K epoxy primers can be directly over coated with:

    • 2K topcoats.
    • 1K basecoats.
    • 2K acrylic primers.
    • 2K polyester body fillers.
    • 2K epoxy body fillers.
  • Informacja
  • General notes
    • Do not exceed recommended doses of the hardener!
      The best repair results can be achieved by painting at room temperature. The temperature in the body shop and the temperature of the product should be similar.
    • When working with 2K products, it is recommended to use personal protection equipment. Protect the eyes and airways.
    • The rooms should be well ventilated.
    • Clean the guns and equipment immediately after use.
    • This product cannot be applied on wash primers and 1K primers.

    Caution: To maintain safety, always follow the instructions given in the MSDS for the products.