V2007 HS 5:1

Acrylic primer

Variants

color nr art. capacity quantity per carton
RAL 7040 grey12380,8 l + 0,16 l6
RAL 7046 dark grey18480,8 l + 0,16 l6
RAL 7012 graphite18500,8 l + 0,16 l6
RAL 9005 black53680,8 l + 0,16 l6
grey1429 3,75 l4
dark grey14223,75 l4
graphite1430 3,75 l4
black 63733,75 l4
hardener14390,75 l4

Gloss grade

semi-mat
V2007 HS 5:1

Video

Description

High-quality 2K acrylic primer with reduced VOC content. HS class product with high resin content and very good filling. Intended for professional car repairs.

Advantages

  • Easy to mix and apply.
  • Very good filling properties.
  • Very good vertical stability.
  • High quality finish.

Substrates

V2007 HS 5:1 acrylic primer can be applied directly on:

  • Steel and aluminum after matting and degreasing.
  • Zinc-coated steel after matting and degreasing.
  • Sanded glass fibre-polyester laminates (GFK/GRP).
  • Polyester body fillers and putties.
  • Epoxy primers.
  • Wash primers.
  • Old paint and original coatings in good condition after matting and degreasing.

Good surface preparation is essential to achieve the best repair results.

Important informations

  • Przetrzeć odtłuścić

    degrease

  • Proporcje mieszania

    mixing proportion
    5 : 1 + 10 +15%

  • Lepkość natryskowa

    spraying viscosity
    30 ÷ 50s / 20°C

  • Żywotność mieszanki

    pot life for the mixture
    45 min. / 20°C

  • Liczba warstw

    2÷3 layers
    HVLP / RP
    ø1,5 ÷ 2,0 mm

  • Czas odparowania

    between layers
    5 ÷ 10 min.

  • Czas odparowania

    before baking
    ~ 10 min.

  • Czas utwardzania

    drying time
    3 h / 20°C
    30 min. / 60°C

  • Szlifowanie na sucho

    P360 ÷ P500

  • Szlifowanie na mokro

    P600 ÷ P1000

Application process

  • Zastosowanie
  • Use

    For car body repair as a high filling primer.

  • Proporcje mieszania
  • Mixing proportion per volume

    Primer: 5
    Hardener: 1
    Thinner: 10÷15%

    Stir thoroughly until obtaining a homogenous mixture.

  • Lepkość natryskowa
  • Spraying viscosity

    30÷50 seconds at 20ºC.

  • Żywotność mieszanki
  • Pot life for the mixture

    about 45 minutes at 20°C

  • Liczba warstw
  • Number of layers

    2÷3 layers. About 70-90 µm for each layer.

    RP gun parameyers
    Nozzle: 1,6÷2,0 mm; Pressure: 2,0-2,2 bar.
    HVLP gun parameters
    Nozzle: 1,5÷1,9 mm; Inlet pressure: 2,0 bar.

  • Czas odparowania
  • Flash off time

    Between layers: about 5÷10 minutes
    Before baking: about 10 minutes

    Flash off time depends on the temperature and coating thickness.

  • Czas utwardzania
  • Drying time

    For a coating thickness of 180 µm:
    about 3 hours at 20°C.
    about 30 minutes at 60°C.
    Temperatures below 20°C significantly increase the drying time.

  • Suszenie promieniem IR
  • IR drying

    10÷15 minutes under short wave for a thickness of 150÷200 µm.
    Do not exceed maximum temperature of 60°C.
    Use according to the recommendations of the equipment manufacturer.
    Wait about 10 minutes before starting IR drying.

  • Szlifowanie na sucho
  • Dry sanding

    Machine sanding: P360÷P500
    Manual sanding: P280÷P360.

  • Szlifowanie na mokro
  • Wet sanding

    Machine sanding: P600÷P1000.
    Manual sanding: P800÷P1000.

  • Informacja
  • Further work

    2K acrylic primers can be directly over coated with:

    • 2K top coats.
    • 1K base coats.
  • Informacja
  • General notes

    • Do not exceed recommended doses of the hardener!
    • The best repair results can be achieved by painting at room temperature. The temperature in the body shop and the temperature of the product should be similar. When working with 2K products, it is recommended to use personal protection equipment. Protect the eyes and airways.
    • The rooms should be well ventilated.
    • Clean the guns and equipment immediately after use.

    Caution: To maintain safety, always follow the instructions given in the MSDS for the products.