Epoxy Primer 10:1

Epoxy primer

Variants

ColorArt. no. Weight Quantity per carton
grey47851 kg + 100 g hardener6

Gloss grade

matt
Epoxy Primer 10:1

Technical documentation

Video

Description

2K epoxy primer designed for car body repairs. It can be applied directly to metal, protecting steel surfaces against corrosion.

Advantages

  • Very high adhesion to various surfaces.
  • Easy to mix and apply.
  • Short hardening time.

Substrates

Epoxy Primer 10:1 can be applied over:

  • Steel and aluminum after flatting and degreasing.
  • Zinc coated steel galvanized steel after flatting and degreasing.
  • Sanded polyester-glass laminates (GFK/GRP) as well as epoxy-glass laminates
  • Polyester and epoxy putties
  • Old finishes in good condition after flatting and degreasing.
  • Good surface preparation is essential to achieve the best repair results.

Important informations

  • Przetrzeć odtłuścić

    degrease

  • Proporcje mieszania

    Mixing ratio
    10 : 1 + 20% ÷ 30%

  • Lepkość natryskowa

    Spraying viscosity
    30 ÷ 50s / 20°C

  • Żywotność mieszanki

    Pot life for the mixture
    1,5 h / 20°C

  • Liczba warstw

    2÷3 layers
    HVLP / RP
    ø1,5 ÷ 2,0 mm

  • Czas odparowania

    between layers
    ~10 min.

  • Czas odparowania

    before baking
    ~ 15 min.

  • Czas utwardzania

    Drying time
    8 h / 20°C
    45 min. / 60°C

  • Szlifowanie na sucho

    P360 ÷ P500

  • Szlifowanie na mokro

    P600 ÷ P1000

Application process

  • Zastosowanie
  • Use

    For car body repairs.

  • Proporcje mieszania
  • Mixing ratio

    By weight
    Primer: 10
    Hardener: 1
    Thinner: 20÷30%

    By volume
    Primer: 10
    Hardener: 1,5
    Thinner: 20÷30%

    Mix thoroughly until a homogeneous consistency is obtained.

  • Lepkość natryskowa
  • Sprayin viscosity

    30÷50 seconds at 20°C

  • Żywotność mieszanki
  • Pot life for the mixture

    about 1,5 hours at 20°C

  • Liczba warstw
  • Number of layers

    2÷3 layers.
    RP gun parameters
    Nozzle: 1,6÷2,0 mm; Pressure: 2,0÷2,2 bar.
    HVLP gun parameters
    Nozzle: 1,5÷1,9 mm; Inlet pressure: 2,0 bar.

  • Czas odparowania
  • Flash off time

    Between layers: approx. 10 minutes
    Before baking: approx. 15 minutes

    Flash off time depends on the temperature and the number of layers.

  • Czas utwardzania
  • Drying time

    about 8 hours at 20°C (depending on the coat thickness)
    about 45 minutes at 60°C (depending on the coat thickness)

    Temperatures below 20°C significantly increases the hardening time.

  • Suszenie promieniem IR
  • IR drying

    10÷15 minutes under short wave for coating thickness of 150÷200 µm.
    Do not exceed maximum temperature of 60°C.
    Use according to the recommendations of the equipment manufacturer.
    Wait about 10 minutes before starting IR drying.

  • Szlifowanie na sucho
  • Dry sanding

    Machine sanding: P360÷P500.
    Manual sanding: P280÷P320.

  • Szlifowanie na mokro
  • Wet sanding

    Machine sanding: P600÷P1000.
    Manual sanding: P800÷P1000.

  • Informacja
  • Further work

    2K epoxy primers can be directly over coated with:

    • 2K top coats
    • 1K base coats.
    • 2K acrylic primers
    • 2K polyester putties.
    • 2K epoxy putties
  • Informacja
  • General notes
    • Do not exceed recommended doses of the hardener!
    • The best repair results can be achieved at room temperature. The temperature in the body shop and the temperature of the product should be similar
    • When working with 2K products, it is recommended to use personal protection equipment. Protect the eyes and air ways.
    • The rooms should be well ventilated.
    • Clean the guns and equipment immediately after use.

    Caution: To maintain safety, always follow the instructions given in the MSDS for the products.

Ask about this product



    

    Related products

      
    See also other products